Taber Rotary Abraser 1700/1750

The TABER® Rotary Platform Abrasion Tester – Model 1700 and 1750 are commonly referred to as the Taber Abraser (Abrader) or Rotary Platform Dual (Double) Head Tester.  First introduced in the 1930’s, this precision built instrument was developed to perform accelerated wear testing.  Since its inception, the Taber Abraser has been used for quality & process control, research & development and material evaluation. Used to test a wide spectrum of materials, the instrument has been referenced in numerous standards and specifications (including plastics, coatings, laminates, leather, paper, ceramics, carpeting, safety glazing, etc.).

PDF  PDF  PDF  PDF

Kategori:

Beskrivning

 

REFERENCED IN MORE THAN 100 INTERNATIONAL
TEST STANDARDS AND SPECIFICATIONS

Easy to operate, the Taber Abraser has been specified by numerous industries as the standard for wear and abrasion research, quality and process control, materials evaluation, and product development. Its field of application includes tests of painted, lacquered, powder coated, and electroplated surfaces; textile fabrics ranging from sheer silks to heavy upholstery and carpeting; solid materials such as metals, stone and ceramics; plus plastics, leather, rubber, linoleum, laminates, glass, paper, and many others.

 

GENUINE TABER ABRADING WHEELS AND
TEST ACCESSORIES OFFER ENORMOUS VERSATILITY

Different grades of standardized abrasive wheels have been engineered to meet varying requirements of abrasive action enabling the instrument to be used to test a diverse range of materials. Available as Calibrase® or Calibrade®, these proprietary abradants are designed so the binder material breaks down during use, exposing new abrasive particles. Optional accessories such as the Grit Feeder or Scuffing Head Attachments can be used to expand the type of test being conducted.

 

Features of the latest Rotary Abraser

  • LCD OPERATOR TOUCH SCREEN
  • QUICK RELEASE WHEEL MOUNTING HUB
  • CRITICAL COMPONENTS EASY TO REPLACE
  • COMPACT ABRASER ARM ASSEMBLIES
    REDESIGNED SUPPORT FRAME AND HOUSING
  • DIRECT FLOW VACUUM NOZZLE WITH
    PRECISION HEIGHT ADJUSTMENT
  • SCREW-IN VACUUM NOZZLE TIPS
    FOR 8 mm AND 11 mm
  • SELECTABLE DISPLAY OPTIONS
    (INCLUDING LANGUAGE)
  • STORE TEST PROFILES

 

Evaluation

There are various techniques used to interpret results generated with the TABER Rotary Platform Abraser (Abrader).  The method of evaluation that you select should reflect the type of material that is being tested. If you are following a specification – the method for interpreting test results will be listed.

The most common methods of evaluating results from the Taber Abraser (Abrader) include:

Cycles to a Specific End-Point – The number of cycles required to reach a predetermined end point, or the appearance or condition of the specimen after a fixed number of cycles.  The evaluation criteria may include: loss in breaking strength, yarn breakage, loss in coating, change in gloss, color loss, or other changes in appearance.  In these cases, the abraded sample is usually compared to a known standard of the material tested.  When visually inspecting changes in specimen appearance, evaluations should be made using an agreed upon rating system such as a visual grading scale (e.g. five-step) or pass/fail criteria.

Weight (Mass) Loss – This technique measures how much material has been removed by abrasion, and is usually reported in milligrams.

      L = A – B

     where L = weight loss

          A = weight (mass) of specimen before abrasion

          B = weight (mass) of specimen after abrasion

When performing the weight loss method, loose particulate may adhere to specimens during testing.  It is critical that you clean off the test specimens as best as possible prior to weighing.

Taber Wear Index – Indicates rate of wear, and is calculated by measuring the loss in weight (in milligrams) per thousand cycles of abrasion. The lower the wear index, the better the abrasion resistance.

      I = [(A – B) * 1000] / C

where I = wear index

            A = weight (mass) of specimen before abrasion

            B = weight (mass) of specimen after abrasion

            C = number of test cycles

Volume Loss – When comparing the wear resistance of materials that have different specific gravities, a correction for the specific gravity of each material should be applied to give a true measure of the comparative wear resistance.  Calculate the wear index as shown above, and divide the result by the material’s specific gravity.  The use of this correction factor provides a wear index related to the loss in volume of the material to which it is applied.  When comparing materials of different specific gravities, test parameters must be the same including wheel selection and load.

Wear Cycles Per Mil (0.001 inch) – Used to express abrasion cycles required to wear through a coating of a known thickness.

      W = D / T

Where W = Wear Cycles Per Mil

            D = number of cycles required to wear coating through to substrate

            T = coating thickness, mils

Depth of Wear – To determine the depth of wear, use a thickness gauge or other appropriate device to measure the specimen thickness on four points along the path to be abraded, approximately 38 mm from the center hole and 90° apart.  Calculate the average of the readings.  After subjecting the specimen to abrasion, repeat the measurements and average the readings.  Calculate the difference.  Alternatively, the depth of the wear can be measured with an instrument such as an Optical Micrometer.

Residual Breaking Force (textile fabrics) – This technique measures the effective strength of the fabric, or force required to break a specific width of fabric.  To determine the individual breaking force of the abraded specimen use the procedure described in the ASTM D5034 and D5035 Standard Test Method for Breaking Strength and Elongation of Textile Fabrics.  [Note, you must change the referenced distance between clamps to 25mm and horizontally place the path of abrasion on the abraded specimen midway between the clamps.]  Report the breaking load to the nearest 0.5kg.

Average Breaking Strength (textile fabrics) – Calculated by averaging the breaking strength of the abraded specimens and the unabraded specimens, as determined by the Residual Breaking Force.

Percentage Loss in Breaking Strength (textile fabrics) – To determine the breaking load of the original fabric and the abraded specimen, use the procedure noted above (ASTM D5034 and D5035).  Calculate the percentage loss in breaking strength to the nearest 1% for each lengthwise and widthwise directions.

      AR% = 100 * (X – Y) / X

where AR% = abrasion resistance, %

               X = breaking force before abrasion, g (lb)

               Y = breaking force after abrasion, g (lb)

 

Standards (most common)

  •  ASTM D3389
  • ASTM D3730
  • ASTM D3884
  • ASTM D4060
  • ASTM D4685
  • ASTM D4712
  • ASTM D5146
  • ASTM D5324
  • ASTM D6037
  • ASTM D7255
  • ASTM F362
  • ASTM F510
  • BS 3900-A7
  • DIN 52347
  • DIN 53109
  • DIN 53754
  • DIN 53799
  • DIN 68861
  • EN 13329(E)
  • EN 13696
  • EN 14431
  • EN 14864
  • EN 438-2
  • EN 660-2
  • ISO 5470
  • ISO 5470-1
  • ISO 7784-2
  • ISO 9352
  • NEN 1857
  • TAPPI T476

 

    Företagsnamn (obligatorisk)

    Ditt namn (obligatorisk)

    Telefonnummer (obligatorisk)

    Din epost (obligatorisk)

    Ditt meddelande

    GDPR Compliance


      Företagsnamn (obligatorisk)

      Ditt namn (obligatorisk)

      Telefonnummer (obligatorisk)

      Din epost (obligatorisk)

      Ditt meddelande

      GDPR Compliance